Insights from collaborative research may lead to improvements in the production of carbon fibres

Infrared (IR) imaging technology at the Australian Synchrotron, developed specifically for carbon fibre analysis, has contributed to a better understanding of chemical changes that affect structure in the production of high-performance carbon fibres using a precursor material.

A research collaboration led by Carbon Nexus, a global carbon fibre research facility at Deakin University, Swinburne University of Technology and members of the Infrared Microspectroscopy team at the Australian Synchrotron, has a paper accepted for publication in the Journal of Materials Chemistry A that identified and helped to explain important structural changes that occur during the production of carbon fibres.

The research was undertaken to elucidate the exact chemical transformation occurring during the heat treatment of polyacrylonitrile (PAN), which produced structural changes.

The majority of commercial carbon fibres are manufactured from PAN but there has been an imperfection that occurred during production that affected its material properties.

Because the conversion of PAN to carbon fibre did not occur evenly across the fibre, it resulted in a skin-core structure.

Manufacturers want to prevent the formation of the skin-core structure in order to enhance the strength of the fibres.

A multitude of experimental techniques including IR spectroscopy confirmed that structural differences evolved along the radial direction of the fibres, which produced the imperfection.

The difference between skin and core in stabilised fibres evolved from differences in the cross linking mechanism of molecular chains from the skin to the core.

The information could potentially help manufacturers improve the production process and lead to better fibres.

Cap and cone characteristics carbon fibres
Chemical distribution of nitrile (C≡N) and C=N functional groups a) 0-min b) 12-min and c) 24-min treated PAN fibres (with 3D contour plots of the corresponding functional groups shown on the right side).

“Using a technique called Attenuated Total Reflection (ATR) to focus the synchrotron beam, the IR beamline allowed the research team to acquire images across individual fibres, to see where carbon-carbon triple bonds in the PAN were being converted to double bonds,” said Dr Mark Tobin, Principal Scientist, IR, at the Australian Synchrotron, who is a co-author with Dr Pimm Vongsvivut and Dr Keith Bambery.

“Previous IR studies have been conducted on fibre bundles and powdered fibres, while we were able to analyse the cross section of single filaments.”

To acquire detailed images of the fibres, which are only 12 microns across, the IR team modified the beamline for the experiment using a highly polished germanium crystal to focus the IR beam onto the fibres.

High resolution synchrotron based maps confirmed that the concentration of nitrile (C≡N) was higher on the areas where the C=N functional groups were lower.

“The nitrile (C≡N) is replaced by C=N as the PAN goes through the process of converting to carbon fibre. This takes place faster in the middle of the fibres, which is why—part way through the process —you see a “ring” of C≡N. The C=N is a peak in the middle,” explained Tobin.

‘Cup and cone’ chemical characteristics captured by IR imaging, also confirmed that a high degree of the reaction to form cyclic structures occurred in the core compared to the skin.

Other experimental techniques, which were undertaken at Carbon Nexus and Factory of the Future at Swinburne University of Technology, included optical microscopy, Raman microspectroscopy, nanoindentation, thermal analysis and tensile testing.
 

Carbon fibre pilot line
Carbon fibre pilot line                                                                                       Image: Carbon Nexus, Deakin University

Carbon Nexus operates the world’s most customised carbon fibre pilot line (shown above).

Lead author Srinivas Nunna received a post graduate research award from the Australian Institute of Nuclear Science and Engineering (AINSE) to support the study.

 

Published: 07/04/2017

Recent articles

See all »

Media enquiry form

If you have a media enquiry please call
Phil McCall: +61 438 619 987

Or

Send »

Please provide us with your name, phone number and
email so we can get back to you.

Error: Enquiry was not sent! Check all fields have been populated correctly.
Success: Enquiry was sent successfully.